Coffee Science
URI permanente desta comunidadehttps://thoth.dti.ufv.br/handle/123456789/3355
Navegar
2 resultados
Resultados da Pesquisa
Item Performance of cross laminated timber panels made of Pinus oocarpa and Coffea arabica waste(Editora UFLA, 2021) Furtini, Ana Carolina Corrêa; Santos, Carolina Aparecida dos; Garcia, Hudson Venâncio Silva; Brito, Flávia Maria Silva; Santos, Thalita Paula dos; Mendes, Lourival Marin; Guimarães Júnior, José BeneditoThe growth of the civil construction sector, made necessary to develop alternative products made of sustainable materials. Within this context came the cross laminated timber panels (CLT), which are formed by gluing veneer arranged at 90°, which provide high strength and great versatility, as constructive elements. This research aimed to evaluate the chemical properties of the particles of both materials and evaluate the performance of CLT panels made with Pinus oocarpa and waste wood from Coffea arabica. The panels were made with three orthogonal layers with veneer of pine and coffee wood, using the phenol-formaldehyde (PF) adhesive with a spread rate of 0.35kgm-² and the hydraulic press with a pressure of 1,2×107 N.m-2for 15 min. The physical, mechanical properties, acoustic and thermal performance of the panels were evaluated. There was a significant difference for water absorption in 2 and 24 hours. The panels produced only with coffee wood waste showed the lowest water absorption rates, corresponding to 10.2 and 33.3%, in 2 and 24 hours. In relation to the MOE, the panels made with varied veneer were statistically equivalent to each other and the panels made of pine blades showed a MOE corresponding to 3,33×107 N.m-2. The same trend was observed for MOR, since the average value obtained for pine panels, corresponding to 1,35x108 N.m-2 was significantly higher. Panels made of coffee veneer and pine veneer showed no delamination. With regard to acoustic and thermal evaluation, all panels met the minimum requirements indicated in the standards, with emphasis on coffee wood waste, associated or not with pine wood.Item Analysis of the coffee peel application over the soil-cement bricks properties(Editora UFLA, 2019-01) Castro, Eliziane Denize de; Villela, Luciana Silva; Mendes, Lourival Marin; Mendes, Rafael Farinassi; Ribeiro, André Geraldo Cornélio; Guimarães Junior, José Benedito; Rabelo, Giovanni FranciscoThe development of materials that use less polluting manufacturing techniques and can be manufactured from agricultural and/or industrial waste is an increasingly explored field of research. The objective of this work was to study the effects of the coffee peel particles (Coffea arabica L.) incorporation in partial replacement of cement, on the physical, mechanical and thermal properties of bricks, at different ages. For this purpose, soil corrected with sand, Portland cement type CP II F-32 and coffee peel particles were used. After the initial percentage of cement in the mixture was defined as 10%, coffee peels were added in relation to cement, equal to 5%, 10%, 15% and 20%. The bricks were submitted to simple compression tests, at the ages of 14, 28 and 56 days, thermal insulation at 28 days. The increase in peel content caused increases in water absorption, and reduction of compressive strength and apparent specific dry mass. The interaction between the shell content and the age of the specimens was significant only for the variable resistance to compression. The thermal conductivity found for the material showed its insulating potential, with values below those determined for ceramic bricks. In general, it can be concluded that the material produced did not fit in the normative requirements for soil-cement bricks, however, the mechanical characteristics found in there, indicate the possibility of use in rustic constructions, such as those ones made with adobe bricks.